C66800 Manganese Bronze
Approx. Rs 750 / Kilogram
- Minimum Order Quantity: 1000 Kilogram
- Composition: Copper
- Material: C66800 Manganese Bronze
- Color: BRonze
- Manganese Bronze Shape: Round
- Tensile Strength: 21
- Product Name: C66800 Manganese Bronze
- Bronze Shape: Round
- Size Thickness: 8mm To 100 mm
- Country of Origin: Made in India
The
Manganese Bronze C66800 alloy possess good hot and cold workability and forging ability. It is fabricated using the process of bending, coining, rawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
Typical Uses: - Industrial: Gears, Sealing Rings, Thrust Bearings, Bushings, Cams, Spindles, Bearings, Idler Pins, Connecting Rods, Drive Shafts, Valve Seats, Sleeve Bearings, Piston Heads.
- Marine: Pump Parts, Hardware, High Strength
Technical Specifications:
Specifications | Designation |
UNS | C67300 |
UNS | C67400 |
UNS | C67420 |
Chemical Composition:
| Cu | Al | Fe | Pb | Mn | Ni | Si | Sn | Zn |
Min./Max. | 60.0-63.0 | 0.25 | 0.35 | 0.5 | 2.0-3.5 | 0.25 | .50-1.5 | 0.3 | Rem. |
Nominal | 61.5 | - | - | - | 2.7 | - | 1 | - | - |
Physical Properties:
Density | 0.300 lb/in3 |
Melting Range | 1690 – 1730 oF |
Coefficient of Expansion | (68 to 572oF) 11 ?in/in oF |
Thermal Conductivity | 55 Btu/ft h oF |
Electrical Conductivity | 21 % IACS |
Electrical Resistivity | 54 ? (circ mil/ft) |
Relative Magnetic Permeability | <1.02 |
Coefficient of Friction | 0.15 |
Additional Information:- Item Code: C66800
- Production Capacity: 6000
- Delivery Time: 5-6
- Packaging Details: Custom and wooden
C67000 Manganese Bronze B
Approx. Rs 750 / Kilogram
- Minimum Order Quantity: 1000 Kilogram
- Composition: Copper
- Brand: Shree Extrusion Limited
- Material: Bronze
- Packaging Type: Box
- Color: Bronze
- Manganese Bronze Shape: Round
- Tensile Strength: Good
- Product Name: C67000
- Bronze Shape: Round
- Size Thickness: 10 To 250
- Country of Origin: Made in India
The
C67000 Manganese Bronze B is high in strength alloy that possesses hot and cold workability with good forging ability. The alloy is manufactured using the process of bending, coining, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
Typical Uses: - Industrial: Forgings, Corrosion Resistance, Wearability , Fatigue Resistance , High Strength .
Technical Specifications:
Specifications | Designation |
ISO | CuAl8Fe3 |
European | CuAl8Fe3 |
BSI | AS 106 |
JIS | C 6140 |
Physical Properties:
Product Property | - |
Melting Point - Liquidus°F | 1652 |
Density lb/cu in. at 68°F | 0.286 |
Specific Gravity | 7.92 |
Electrical Conductivity% IACS at 68°F | 22 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 57 |
Coefficient of Thermal Expansion 68-57210?6 per °F (68 – 572°F) | 11.9 |
Additional Information:- Item Code: C670MnBr
- Production Capacity: 100 Ton
- Delivery Time: 4-5 week
- Packaging Details: Box
C67300 Manganese Bronze
Approx. Rs 750 / Kilogram
- Minimum Order Quantity: 1000 Kilogram
- Composition: Copper
- Brand: Shree Extrusion Limited
- Packaging Type: Box
- Material: Bronze
- Color: Bronze
- Manganese Bronze Shape: Round
- Tensile Strength: Good
- Product Name: SEL Bronze
- Bronze Shape: Round
- Country of Origin: Made in India
The
C67300 Manganese Bronze is high in strength alloy with good bearing qualities. The alloy maintains high impact resistance with good machinability by making it well suited for clutch bearings, shaft bushings, sleeve bearings, thrust bearings, pump parts, drive shafts, bearing pins, wear plates, gears and cams. It also resists squashing out under high loads and extreme wear applications.
Typical Uses: - Fasteners: Fasteners, Lead Screw Nuts
- Industrial: Gears and Cams, Wear Plates, Bushings, Seal Rings, Idler Pins, Piston Heads, Brearing Pins, Thrust Bearings, Sleeve Bearings, Propeller Shafts, Shaft Bushings, Clutch Bearings, Drive Shafts, Spindles, Pump Parts, Bearings
- Marine: Hardware, Valve Seats
- Other: Connecting Rods
Technical Specifications:
Specifications | Designation |
UNS | C66800 |
UNS | C67400 |
UNS | C67420 |
Chemical Composition:
| Al | Cu | Fe | Pb | Mn | Ni | Si | Sn | Zn |
Min/Max | 0.25 | 58.0 - 63.0 | 0.5 | 0.40 - 3.0 | 2.0 - 3.5 | 0.25 | 0.50 - 1.5 | 0.3 | Rem |
Nominals | - | 60.5000 | - | 1.7000 | 2.7000 | - | 1.0000 | - | 34.1000 |
Specifications:
End Product | Specification |
Bar | SAE J461, J463 |
Forgings | SAE J461, J463 |
Rod | SAE J463, J461 |
Shapes | SAE J463, J461 |
Fabrication:
Joining Technique | Suitability |
Machinability Rating | 70 |
Physical Properties:
Product Property | US Customary | Metric |
Coefficient of Thermal Expansion | 11 ·10-6 per oF (68-572 F) | 19.0 ·10-6 per oC (20-300 C) |
Density | .30 lb/in3 at 68 F | 8.3 gm/cm3 @ 20 C |
Electrical Conductivity | 22 %IACS @ 68 F | 0.13 MegaSiemens/cm @ 20 C |
Melting Point - Liquidus | 1605 F | 874 C |
Modulas of Elasticity in Tension | 17000 ksi | 117200 MPa |
Specific Gravity | 8.3 | 8.3 |
Thermal Conductivity | 55 Btu · ft/(hr · ft2·oF)at 68F | 95.0 W/m · oK at 20 C |
Additional Information:- Item Code: C67300
- Production Capacity: 100 Ton
- Delivery Time: 4-5 Week
- Packaging Details: Box
C67400 Manganese Bronze
Approx. Rs 750 / Kg
- Minimum Order Quantity: 1000 Kg
- Composition: Copper
- Brand: Shree Extrusion Limited
- Thickness: 10 MM MIN
- Material: Bronze
- Packaging Type: BOX AND CUSTOME
- Color: YELLOW
- Manganese Bronze Shape: ROUND TUBE
- Tensile Strength: GOOD
- Product Name: C67400
- Padhni Grade: C674
- Bronze Shape: ROUND TUBE
- Size Thickness: ROUND THICK
- Country of Origin: Made in India
The
Manganese BronzeC67400alloy is manufactured using the process of bending, drawing, upsetting, and many other processes. The alloy is excellent on hot and cold workability and forges ability.
Typical Uses:- Industrial: Bushings, Shafts, Cams, Chain Guides, Wear Plates, Gears, Food Conveyor Chain
- Other: Connecting Rods
Technical Specifications:
Specifications | Designation |
UNS | C66800 |
UNS | C67300 |
UNS | C67420 |
Chemical Composition:
| Al | Cu | Fe | Pb | Mn | Ni | Si | Sn | Zn |
Min/Max | 0.50 - 2.0 | 57.0 - 60.0 | 0.35 | 0.5 | 2.0 - 3.5 | 0.25 | 0.50 - 1.5 | 0.3 | Rem |
Nominals | 1.2 | 58.5 | - | - | 2.8 | - | 1 | - | 36.5 |
Specifications:
End Product | Specification |
Bar | SAE J461, J463 |
Forging | SAE J461, J463 |
Rod | SAE J463, J461 |
Shapes | SAE J463, J461 |
Fabrication:
Joining Technique | Suitability |
Brazing | Good |
Butt Weld | Good |
Capacity for Being Cold Worked | Poor |
Capacity for Being Hot Formed | Excellent |
Coated Metal Arc Welding | Not Recommended |
Forgeability | 100 |
Gas Shielded Arc Welding | Fair |
Machinability Rating | 30 |
Oxyacetylene Welding | Not Recommended |
Seam Weld | Good |
Soldering | Fair |
Spot Weld | Good |
Physical Properties:
Product Property | US Customary | Metric |
Coefficient of Thermal Expansion | 11.0 ·10-6 per oF (68-572 F) | 19.8 ·10-6 per oC (20-300 C) |
Density | 0.292 lb/in3 at 68 F | 8.08 gm/cm3 @ 20 C |
Electrical Conductivity | 23 %IACS @ 68 F | 0.135 MegaSiemens/cm @ 20 C |
Electrical Resistivity | 45.1 ohms-cmil/ft @ 68 F | 7.5 microhm-cm @ 20 C |
Melting Point - Liquidus | 1625 F | 885 C |
Melting Point - Solidus | 1590 F | 866 C |
Modulus of Elasticity in Tension | 16000 ksi | 110000 Mpa |
Modulus of Rigidity | 6000 ksi | 41370 Mpa |
Specific Gravity | 8.08 | 8.08 |
Specific Heat Capacity | 0.09 Btu/lb/oF at 68 F | 377.1 J/kg/ · oK at 293 K |
Thermal Conductivity | 58.0 Btu · ft/(hr · ft2·oF)at 68F | 100.4 W/m · oK at 20 C |
Additional Information:- Item Code: C674
- Production Capacity: 100 TON
- Delivery Time: 3-4 WEEK
- Packaging Details: BOX
C67500 Manganese Bronze
Approx. Rs 750 / Kilogram
- Minimum Order Quantity: 1000 Kilogram
- Composition: Copper
- Brand: Shree Extrusion Limited
- Packaging Type: Box
- Material: Bronze
- Color: Bronze
- Manganese Bronze Shape: Round
- Tensile Strength: Good
- Product Name: C67500
- Bronze Shape: Round
- Size Thickness: 10 to 250
- Country of Origin: Made in India
Alloy
C67500 Manganese Bronze is a wrought alloy with additions of iron, tin and manganese to increase the strength and corrosion resistance. It can be worked to increase the strength and can be available in the half hard and fully hard condition. It possesses hot working properties and can be die forged into valves, connectors and other components for military applications. It can also be hot-headed or upset forged for manufacturing fasteners.
Typical Uses: - Automotive: Clutch Disks, Shafting, Pump Rods
- Fasteners: bolts
- Industrial: Valve Bodies, Balls, Valve Stems, Bushings, Aircraft Parts
- Marine: hardware
Chemical Composition:
| Al | Cu | Fe | Pb | Mn | Si | Zn |
Min/Max | 0.25 | 57.0 - 60.0 | 0.80 - 2.0 | 0.2 | 0.05 - 0.50 | 0.50 - 1.5 | Rem |
Nominals | - | 58.5000 | 1.4000 | - | 0.1000 | 1.0000 | 39.0000 |
Specifications:
End Product | Specification |
Bar | ASTM B138, SAE J461, J463 |
Bar, Forging | ASTM B124 |
Bolts | ASTM F468 |
Forgings, Die | ASTM B283, SAE J463, J461 |
Nuts | ASTM F467 |
Rod | ASTM B138, SAE J463, J461 |
Rod, Forging | ASTM B124 |
Screws | ASTM F468 |
Shapes | ASTM B138, SAE J461, J463 |
Shapes, Forging | ASTM B124 |
Studs | ASTM F468 |
Fabrication:
Joining Technique | Suitability |
Brazing | Excellent |
Butt Weld | Good |
Capacity for Being Cold Worked | Poor |
Capacity for Being Hot Formed | Excellent |
Coated Metal Arc Welding | Not Recommended |
Forgeability | 80 |
Gas Shielded Arc Welding | Fair |
Machinability Rating | 30 |
Oxyacetylene Welding | Good |
Seam Weld | Fair |
Soldering | Excellent |
Spot Weld | Good |
Additional Information:- Item Code: C67500
- Production Capacity: 100 Ton
- Delivery Time: 4-5 week
- Packaging Details: Box
C67600 Manganese Bronze
Approx. Rs 750 / Kilogram
- Minimum Order Quantity: 1000 Kilogram
- Composition: Copper
- Brand: Shree Extrusion Limited
- Thickness: 10 TO 250
- Packaging Type: BOX
- Material: Bronze
- Color: BRONZE
- Manganese Bronze Shape: ROUND
- Tensile Strength: GOOD
- Product Name: C67600
- Bronze Shape: ROUND
- Size Thickness: 10 TO 250
- Country of Origin: Made in India
The alloy possesses excellent hot and cold workability good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
Typical Uses:
- Industrial: Gate Valve Stems, Welding Rod, Valve Balls
Chemical Composition:
| Cu | Fe | Pb | Mn | Sn | Zn |
Min/Max | 57.0 - 60.0 | 0.40 - 1.3 | 0.50 - 1.0 | 0.05 - 0.50 | 0.50 - 1.5 | Rem |
Nominals | 58.5 | 0.8 | 0.7 | 0.27 | 1 | 38.7 |
Specifications:
End Product | Specification |
Brazing Filler Metal | AWS A5.8 |
Forgings, Die | ASTM B283 |
Fabrication:
Joining Technique | Suitability |
Brazing | Excellent |
Capacity for Being Cold Worked | Poor |
Capacity for Being Hot Formed | Excellent |
Forgeability | 80 |
Gas Shielded Arc Welding | Fair |
Machinability Rating | 60 |
Oxyacetylene Welding | Good |
Soldering | Excellent |
Spot Weld | Good |
Physical Properties:
Product Property | US Customary | Metric |
Coefficient of Thermal Expansion | 11.8 ·10-6 per oF (68-572 F) | 20.4 ·10-6 per oC (20-300 C) |
Density | 0.302 lb/in3 at 68 F | 8.36 gm/cm3 @ 20 C |
Electrical Conductivity | 24 %IACS @ 68 F | 0.139 MegaSiemens/cm @ 20 C |
Melting Point - Liquidus | 1630 F | 890 C |
Melting Point - Solidus | 1590 F | 865 C |
Modulus of Elasticity in Tension | 15000 ksi | 103400 Mpa |
Modulus of Rigidity | 5600 ksi | 38600 Mpa |
Thermal Conductivity | 61.0.0 Btu · ft/(hr · ft2·oF)at 68F | 105.7 W/m · oK at 20 C |
Additional Information:- Item Code: C67600
- Production Capacity: 100 TON
- Delivery Time: 3-4 WEEK
- Packaging Details: BOX
C86200 Manganese Bronze
Approx. Rs 750 / Kilogram
- Minimum Order Quantity: 1000 Kilogram
- Composition: Copper
- Brand: Shree Extrusion Limited
- Material: Bronze
- Packaging Type: Box
- Color: Bronze
- Manganese Bronze Shape: Round
- Tensile Strength: Good
- Product Name: C86200 Mn Bronze
- Bronze Shape: Round
- Country of Origin: Made in India
The Manganese bronze copper casting alloy UNS C86200 consists primarily of copper, zinc, aluminium and manganese bronze. Manganese existing in UNS C86200 provides an attractive chocolate brown colour which is commonly used in architecture. The presence of lead in the alloy improves the longevity of the alloy.
Typical Uses: - Builders: Hardware Brackets, Structural Parts
- Fasteners: Screw Down Nuts
- Industrial: Struts, Gears, Valve Stems, Bushings, Cams, Wear Rings for Pressing Dies for Wood Pulp Industry, High Strength Machine Parts, Hooks, Frames, Shafts, Marine Racing Propellers, Worm Gears, Pressing Dies for Wood Pulp
- Marine: Rudders, Marine Castings, Boat Parts, Clamps
Technical Specification:
Specifications | Designation |
UNS | C86200 |
ISO | CuZn26Al4Fe3Mn3 |
JIS | CAC303 |
Chemical Composition:
| Zn | Cu | Fe | Mn | Ni | Pb | Sn |
Min/Max | 22-28 | 60-66 | 2-4 | 2.5-5 | 1.0max | 0.2max | 0.2 max |
Nominals | 25 | 63 | 3 | 3.7 | - | - | - |
Physical Properties:
Product Property | US Customary |
Melting Point - Liquidus | 1725 F |
Melting Point - Solidus | 1650 F |
Density | 0.288 lb/in3 at 68 F |
Specific Gravity | 7.97 |
Electrical Resistivity | 136.70 ohms-cmil/ft @ 68 F |
Electrical Conductivity | 8 %IACS @ 68 F |
Thermal Conductivity | 20.50 Btu · ft/(hr · ft2·°F)at 68F |
Coefficient of Thermal Expansion | 120 ·10-6 per oF (68-392 F) |
Specific Heat Capacity | 0.090 Btu/lb/°F at 68 F |
Modulus of Elasticity in Tension | 15000 ksi |
Magnetic Permeability* | 1.24 |
Additional Information:- Item Code: C862
- Production Capacity: 100 Ton
- Delivery Time: 4-5 week
- Packaging Details: Box
C67300 Manganese Bronze Rods
Approx. Rs 750 / Kilogram
- Minimum Order Quantity: 1000 Kilogram
- Material: Bronze
- Brand: Shree Extrusion Limited
- Grade: C67300
- Usage: Manufacturing
- Country of Origin: Made in India
The
C67300 Manganese Bronze is high in strength alloy with good bearing qualities. The alloy maintains high impact resistance with good machinability by making it well suited for clutch bearings, shaft bushings, sleeve bearings, thrust bearings, pump parts, drive shafts, bearing pins, wear plates, gears and cams. It also resists squashing out under high loads and extreme wear applications.
Typical Uses: - Fasteners: Fasteners, Lead Screw Nuts
- Industrial: Gears and Cams, Wear Plates, Bushings, Seal Rings, Idler Pins, Piston Heads, Brearing Pins, Thrust Bearings, Sleeve Bearings, Propeller Shafts, Shaft Bushings, Clutch Bearings, Drive Shafts, Spindles, Pump Parts, Bearings
- Marine: Hardware, Valve Seats
- Other: Connecting Rods
Technical Specifications:
Specifications | Designation |
UNS | C66800 |
UNS | C67400 |
UNS | C67420 |
Chemical Composition:
| Al | Cu | Fe | Pb | Mn | Ni | Si | Sn | Zn |
Min/Max | 0.25 | 58.0 - 63.0 | 0.5 | 0.40 - 3.0 | 2.0 - 3.5 | 0.25 | 0.50 - 1.5 | 0.3 | Rem |
Nominals | - | 60.5000 | - | 1.7000 | 2.7000 | - | 1.0000 | - | 34.1000 |
Specifications:
End Product | Specification |
Bar | SAE J461, J463 |
Forgings | SAE J461, J463 |
Rod | SAE J463, J461 |
Shapes | SAE J463, J461 |
Fabrication:
Joining Technique | Suitability |
Machinability Rating | 70 |
Physical Properties:
Product Property | US Customary | Metric |
Coefficient of Thermal Expansion | 11 ·10-6 per oF (68-572 F) | 19.0 ·10-6 per oC (20-300 C) |
Density | .30 lb/in3 at 68 F | 8.3 gm/cm3 @ 20 C |
Electrical Conductivity | 22 %IACS @ 68 F | 0.13 MegaSiemens/cm @ 20 C |
Melting Point - Liquidus | 1605 F | 874 C |
Modulas of Elasticity in Tension | 17000 ksi | 117200 MPa |
Specific Gravity | 8.3 | 8.3 |
Thermal Conductivity | 55 Btu · ft/(hr · ft2·oF)at 68F | 95.0 W/m · oK at 20 C |
C66800 Manganese Bronze Rods
Approx. Rs 750 / Kilogram
- Minimum Order Quantity: 1000 Kilogram
- Diameter: 4 inches
- Shape: Round
- Material: Bronze
- Brand: Shree Extrusion Limited
- Grade: C66800
The
Manganese Bronze C66800 alloy possess good hot and cold workability and forging ability. It is fabricated using the process of bending, coining, rawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
Typical Uses: - Industrial: Gears, Sealing Rings, Thrust Bearings, Bushings, Cams, Spindles, Bearings, Idler Pins, Connecting Rods, Drive Shafts, Valve Seats, Sleeve Bearings, Piston Heads.
- Marine: Pump Parts, Hardware, High Strength
Technical Specifications:
Specifications | Designation |
UNS | C67300 |
UNS | C67400 |
UNS | C67420 |
Chemical Composition:
| Cu | Al | Fe | Pb | Mn | Ni | Si | Sn | Zn |
Min./Max. | 60.0-63.0 | 0.25 | 0.35 | 0.5 | 2.0-3.5 | 0.25 | .50-1.5 | 0.3 | Rem. |
Nominal | 61.5 | - | - | - | 2.7 | - | 1 | - | - |
Physical Properties:
Density | 0.300 lb/in3 |
Melting Range | 1690 – 1730 oF |
Coefficient of Expansion | (68 to 572oF) 11 ?in/in oF |
Thermal Conductivity | 55 Btu/ft h oF |
Electrical Conductivity | 21 % IACS |
Electrical Resistivity | 54 ? (circ mil/ft) |
Relative Magnetic Permeability | <1.02 |
Coefficient of Friction | 0.15 |
Additional Information:- Item Code: C668
- Production Capacity: 60000
- Delivery Time: 5-6 WEEL
- Packaging Details: WOODENCASE
C67500 Manganese Bronze Rods
Approx. Rs 750 / Kilogram
- Minimum Order Quantity: 1000 Kilogram
- Size/Diameter: 4 inch
- Diameter: 4 inches
- Shape: Round
- Material: Bronze
- Single Piece Length: 3 meter
- Usage/Application: Manufacturing
- Customization: Customized
- Brand: Shree Extrusion Limited
- Grade: C67500
- Country of Origin: Made in India
Alloy
C67500 Manganese Bronze is a wrought alloy with additions of iron, tin and manganese to increase the strength and corrosion resistance. It can be worked to increase the strength and can be available in the half hard and fully hard condition. It possesses hot working properties and can be die forged into valves, connectors and other components for military applications. It can also be hot-headed or upset forged for manufacturing fasteners.
Typical Uses: - Automotive: Clutch Disks, Shafting, Pump Rods
- Fasteners: bolts
- Industrial: Valve Bodies, Balls, Valve Stems, Bushings, Aircraft Parts
- Marine: hardware
Chemical Composition:
| Al | Cu | Fe | Pb | Mn | Si | Zn |
Min/Max | 0.25 | 57.0 - 60.0 | 0.80 - 2.0 | 0.2 | 0.05 - 0.50 | 0.50 - 1.5 | Rem |
Nominals | - | 58.5000 | 1.4000 | - | 0.1000 | 1.0000 | 39.0000 |
Specifications:
End Product | Specification |
Bar | ASTM B138, SAE J461, J463 |
Bar, Forging | ASTM B124 |
Bolts | ASTM F468 |
Forgings, Die | ASTM B283, SAE J463, J461 |
Nuts | ASTM F467 |
Rod | ASTM B138, SAE J463, J461 |
Rod, Forging | ASTM B124 |
Screws | ASTM F468 |
Shapes | ASTM B138, SAE J461, J463 |
Shapes, Forging | ASTM B124 |
Studs | ASTM F468 |
Fabrication:
Joining Technique | Suitability |
Brazing | Excellent |
Butt Weld | Good |
Capacity for Being Cold Worked | Poor |
Capacity for Being Hot Formed | Excellent |
Coated Metal Arc Welding | Not Recommended |
Forgeability | 80 |
Gas Shielded Arc Welding | Fair |
Machinability Rating | 30 |
Oxyacetylene Welding | Good |
Seam Weld | Fair |
Soldering | Excellent |
Spot Weld | Good |
Additional Information:- Item Code: C675
- Production Capacity: 100 Ton
- Delivery Time: 4-5 week
- Packaging Details: Box
C67400 Manganese Bronze Rods
Approx. Rs 750 / Kg
- Minimum Order Quantity: 1000 Kg
- Diameter: 4 inches
- Size/Diameter: 4 inch
- Shape: Round
- Material: Bronze
- Single Piece Length: 3 meter
- Usage/Application: Manufacturing
- Customization: Customized
- Brand: Shree Extrusion Limited
- Grade: C67400
- Country of Origin: Made in India
The
Manganese BronzeC67400alloy is manufactured using the process of bending, drawing, upsetting, and many other processes. The alloy is excellent on hot and cold workability and forges ability.
Typical Uses:- Industrial: Bushings, Shafts, Cams, Chain Guides, Wear Plates, Gears, Food Conveyor Chain
- Other: Connecting Rods
Technical Specifications:
Specifications | Designation |
UNS | C66800 |
UNS | C67300 |
UNS | C67420 |
Chemical Composition:
| Al | Cu | Fe | Pb | Mn | Ni | Si | Sn | Zn |
Min/Max | 0.50 - 2.0 | 57.0 - 60.0 | 0.35 | 0.5 | 2.0 - 3.5 | 0.25 | 0.50 - 1.5 | 0.3 | Rem |
Nominals | 1.2 | 58.5 | - | - | 2.8 | - | 1 | - | 36.5 |
Specifications:
End Product | Specification |
Bar | SAE J461, J463 |
Forging | SAE J461, J463 |
Rod | SAE J463, J461 |
Shapes | SAE J463, J461 |
Fabrication:
Joining Technique | Suitability |
Brazing | Good |
Butt Weld | Good |
Capacity for Being Cold Worked | Poor |
Capacity for Being Hot Formed | Excellent |
Coated Metal Arc Welding | Not Recommended |
Forgeability | 100 |
Gas Shielded Arc Welding | Fair |
Machinability Rating | 30 |
Oxyacetylene Welding | Not Recommended |
Seam Weld | Good |
Soldering | Fair |
Spot Weld | Good |
Physical Properties:
Product Property | US Customary | Metric |
Coefficient of Thermal Expansion | 11.0 ·10-6 per oF (68-572 F) | 19.8 ·10-6 per oC (20-300 C) |
Density | 0.292 lb/in3 at 68 F | 8.08 gm/cm3 @ 20 C |
Electrical Conductivity | 23 %IACS @ 68 F | 0.135 MegaSiemens/cm @ 20 C |
Electrical Resistivity | 45.1 ohms-cmil/ft @ 68 F | 7.5 microhm-cm @ 20 C |
Melting Point - Liquidus | 1625 F | 885 C |
Melting Point - Solidus | 1590 F | 866 C |
Modulus of Elasticity in Tension | 16000 ksi | 110000 Mpa |
Modulus of Rigidity | 6000 ksi | 41370 Mpa |
Specific Gravity | 8.08 | 8.08 |
Specific Heat Capacity | 0.09 Btu/lb/oF at 68 F | 377.1 J/kg/ · oK at 293 K |
Thermal Conductivity | 58.0 Btu · ft/(hr · ft2·oF)at 68F | 100.4 W/m · oK at 20 C |
Additional Information:- Item Code: C67400
- Production Capacity: 100 Ton
- Delivery Time: 4-5 W
- Packaging Details: Box
C67000 Manganese Bronze B Rods
Approx. Rs 750 / Kilogram
- Minimum Order Quantity: 1000 Kilogram
- Composition: Copper
- Brand: Shree Extrusion Limited
- Packaging Type: Box
- Material: Bronze
- Color: BRonze
- Usage: Manufacturing
- Manganese Bronze Shape: Round
- Tensile Strength: Good
- Product Name: C67000
- Bronze Shape: Round
- Size Thickness: 10 to 250
- Country of Origin: Made in India
The
C67000 Manganese Bronze B is high in strength alloy that possesses hot and cold workability with good forging ability. The alloy is manufactured using the process of bending, coining, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
Typical Uses: - Industrial: Forgings, Corrosion Resistance, Wearability , Fatigue Resistance , High Strength .
Technical Specifications:
Specifications | Designation |
ISO | CuAl8Fe3 |
European | CuAl8Fe3 |
BSI | AS 106 |
JIS | C 6140 |
Physical Properties:
Product Property | - |
Melting Point - Liquidus°F | 1652 |
Density lb/cu in. at 68°F | 0.286 |
Specific Gravity | 7.92 |
Electrical Conductivity% IACS at 68°F | 22 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 57 |
Coefficient of Thermal Expansion 68-57210?6 per °F (68 – 572°F) | 11.9 |
Additional Information:- Item Code: C67000
- Production Capacity: 100 Ton
- Delivery Time: 4-5 Week
- Packaging Details: Box
C86200 Manganese Bronze Rods
Approx. Rs 750 / Kilogram
- Minimum Order Quantity: 1000 Kilogram
- Single Piece Length: 3 meter
- Usage: Manufacturing
- Material: Bronze
- Brand: Shree Extrusion Limited
- Grade: C86200
The Manganese bronze copper casting alloy UNS C86200 consists primarily of copper, zinc, aluminium and manganese bronze. Manganese existing in UNS C86200 provides an attractive chocolate brown colour which is commonly used in architecture. The presence of lead in the alloy improves the longevity of the alloy.
Typical Uses: - Builders: Hardware Brackets, Structural Parts
- Fasteners: Screw Down Nuts
- Industrial: Struts, Gears, Valve Stems, Bushings, Cams, Wear Rings for Pressing Dies for Wood Pulp Industry, High Strength Machine Parts, Hooks, Frames, Shafts, Marine Racing Propellers, Worm Gears, Pressing Dies for Wood Pulp
- Marine: Rudders, Marine Castings, Boat Parts, Clamps
Technical Specification:
Specifications | Designation |
UNS | C86200 |
ISO | CuZn26Al4Fe3Mn3 |
JIS | CAC303 |
Chemical Composition:
| Zn | Cu | Fe | Mn | Ni | Pb | Sn |
Min/Max | 22-28 | 60-66 | 2-4 | 2.5-5 | 1.0max | 0.2max | 0.2 max |
Nominals | 25 | 63 | 3 | 3.7 | - | - | - |
Physical Properties:
Product Property | US Customary |
Melting Point - Liquidus | 1725 F |
Melting Point - Solidus | 1650 F |
Density | 0.288 lb/in3 at 68 F |
Specific Gravity | 7.97 |
Electrical Resistivity | 136.70 ohms-cmil/ft @ 68 F |
Electrical Conductivity | 8 %IACS @ 68 F |
Thermal Conductivity | 20.50 Btu · ft/(hr · ft2·°F)at 68F |
Coefficient of Thermal Expansion | 120 ·10-6 per oF (68-392 F) |
Specific Heat Capacity | 0.090 Btu/lb/°F at 68 F |
Modulus of Elasticity in Tension | 15000 ksi |
Magnetic Permeability* | 1.24 |