C31400 Leaded Commercial Bronze Rods
Approx. Rs 750 / Kg
- Minimum Order Quantity: 1000 Kg
- Diameter: 4 inches
- Size/Diameter: 6mm - 250mm
- Shape: Round
- Single Piece Length: 3 meters up, 3 meter
- Usage/Application: Manufacturing
- Customization: Customized
- Grade: C31400
- Country of Origin: Made in India
- Forgeability Rating: 90
The C31400 Leaded Commercial Bronze is the combination of natural corrosion resistance with the machining ability of leaded brass. It is the combination of 89% copper and 9% zinc and also contains 2% lead that provides free-cutting characteristics. The low zinc content provides corrosion resistance in potable water with a golden colour The alloy is suitable for outdoor use owing to its resistance towards stress corrosion cracking and where the highest strength is not required.
Specifications:
| End Product | Specification |
| Bar | ASTM B140 |
| Rod | ASTM B140 |
| Shapes | ASTM B140 |
| Valves | MILITARY MIL-V-18436 |
Chemical Composition:
| Cu | Fe | Pb | Ni | Zn | |
| Min/Max | 87.5 - 90.5 | 0.1 | 1.3 - 2.5 | 0.7 | Rem |
| Nominals | 89 | - | 1.9 | - | 9.1 |
Fabrication:
| Joining Technique | Suitability |
| Brazing | Good |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Poor |
| Coated Metal Arc Welding | Not Recommended |
| Gas Sheilded Arc Welding | Not Recommended |
| Machinability rating | 80 |
| Oxyacetylene Welding | Not Recommended |
| Seam Weld | Not Recommended |
| Soldering | Excellent |
| Spot Weld | Not Recommended |
Physical Properties:
| Product Property | US Customary | Metric |
| Coefficient of Thermal Expansion | 10.2 ·10-6 per oF (68-572 F) | 18.4 · 10 6? per °C (20-300 C) |
| Density | 0.319 lb/in3 @ 68 F | 8.83 gm/cm3 @ 20 C |
| Electrical Conductivity | 42 %IACS @ 68 F | 0.246 Mega Siemens/cm @ 20 C |
| Electrical Resistivity | 24.7 ohms-cmil/ft @ 68 F | 4.11 microhm-cm @ 20 C |
| Melting Point Liquid US | 1900 F | 1038 C |
| Melting Point Solid US | 1850 F | 1010 C |
| Modulas of Elasticity in Tension | 17000 ksi | 117000 MPa |
| Modulas of Rigidity | 6400 ksi | 44130 MPa |
| Specific Gravity | 8.83 | 8.83 |
| Specific Heat Capacity | 0.09 Btu/lb/°F @ 68 F | 377.1 J/kg · °K at 293 K |
| Thermal Conductivity | 104.0 Btu · ft/(hr · ft2 ·°F) @ 68 F | 180.0 W/m · °K at 20 C |
Additional Information:
- Item Code: C31400
- Production Capacity: 100 Ton
- Delivery Time: 4-5 W
- Packaging Details: Box
C31600 Nickel Leaded Commercial Bronze
Approx. Rs 750 / Kg
- Minimum Order Quantity: 1000 Kg
- Composition: Copper
- Size/Diameter: 6mm To 130 mm
- Single Piece Length: 3 meter, 3-6m
- Material: Bronze
- Thickness: 10 To 250
- Color: Bronze
- Packaging Type: Rods
- Size: 10 To 250
- Application: Manufacturing
- Bronze Shape: Round
- Finish: Good
- Form: Rod
- Grade: C31600
- Length: 2-3 M
- Country of Origin: Made in India
- Copper (Min): 87.5 - 90.5
The C Nickel Leaded Commercial Bronze C31600 is the combination of 89% copper, 8% zinc, 2% lead and also contains 1% nickel. The alloy is resistant towards corrosion with higher tensile and yield strength, which is the result of the addition of nickel to the alloy. The alloy is resistant towards stress cracking and is suitably be used in high strength outdoor applications.
Specifications:
| End Product | Specification |
| Bar | ASTM B140 |
| Rod | ASTM B140 |
| Shapes | ASTM B140 |
| Valves | MILITARY MIL-V-18436 |
Chemical Composition:
| Cu | Fe | Pb | Ni | P | Zn | |
| Min/Max | 87.5 - 90.5 | 0.1 | 1.3 - 2.5 | 0.7 - 1.2 | 0.04 - 0.1 | Rem |
| Nominals | 89.0000 | - | 1.9000 | 1.0000 | 0.7000 | 8.1000 |
Fabrication:
| Joining Technique | Suitability |
| Brazing | Good |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Poor |
| Coated Metal Arc Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Machinability rating | 80 |
| Oxyacetylene Welding | Not Recommended |
| Seam Weld | Not Recommended |
| Soldering | Excellent |
| Spot Weld | Not Recommended |
Physical Properties:
| Product Property | US Customary | Metric |
| Coefficient of Thermal Expansion | 10.2 ·10-6 per oF (68-572 F) | 18.4 · 10 6? per °C (20-300 C) |
| Density | 0.32 lb/in3 @ 68 F | 8.86 gm/cm3 @ 20 C |
| Electrical Conductivity | 32 %IACS @ 68 F | 0.187 MegaSiemens/cm @ 20 C |
| Electrical Resistivity | 32.4 ohms-cmil/ft @ 68 F | 5.39 microhm-cm @ 20 C |
| Melting Point Liquid US | 1900 F | 1038 C |
| Melting Point Solid US | 1850 F | 1010 C |
| Modulus of Elasticity in Tension | 17000 ksi | 117000 Mpa |
| Specific Gravity | 8.86 | 8.86 |
| Specific Heat Capacity | 0.09 Btu/lb/°F @ 68 F | 377.1 J/kg · °K at 293 K |
| Thermal Conductivity | 81.0 Btu · ft/(hr · ft2 ·°F) @ 68 F | 140.2 W/m · °K at 20 C |
Additional Information:
- Item Code: C31600
- Production Capacity: 100 Ton
- Delivery Time: 4-5 W
- Packaging Details: Box
C19160 Leaded Nickel Copper Rods
Approx. Rs 580 / Kilogram
- Minimum Order Quantity: 1000 Kilogram
- Composition: CuNi10Fe1Mn
- Type: Rods
- Grade: C19160
- Product Type: Rod
- Usage/Application: INDUSTRIAL
- Alloy: Yes
- Country of Origin: Made in India
Leaded Nickel Copper C19160 alloy is a free-cutting bronze alloy, which is mainly used for manufacturing connectors in the electronics industry. The alloy is high on machining ability and is appreciated for high strength, electrical conductivity and corrosion resistance.
Applications:
- Electrical Applications: Contacts, Sockets, Connector Pins
- Density Applications: 0.320 lb/in3 at 68 F
Chemical Composition:
| Cu (1) | Fe | Pb | Ni | P | Sn | Zn | |
| Min/Max | Rem. | 0.05 | .8 - 1.2 | .8 - 1.2 | .15 - .35 | 0.05 | 0.5 |
| Nominals | 97.8 | - | 1 | 1 | 0.2 | - | - |
Fabrication:
| Joining Technique | Suitability |
| Brazing | Good |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Poor |
| Coated Metal Arc Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Machinability rating | 80 |
| Oxyacetylene Welding | Not Recommended |
| Seam Weld | Not Recommended |
| Soldering | Excellent |
| Spot Weld | Not Recommended |
Physical Properties:
| US Customary | Metric | |
| Melting Point - Liquidus | 1980 F | 1082 C |
| Melting Point - Solidus | 1900 F | 1038 C |
| Density | 0.320 lb/in³ at 68 F | 8.88 gm/cm³ @ 20 C |
| Specific Gravity | 8.88 | 8.88 |
| Electrical Conductivity | 55 %IACS @ 68 F | 0.318 MegaSiemens/cm @ 20 C |
| Thermal Conductivity | 146 Btu ft/(hr ft2oF)at 68F | 253.0 W/m oK at 20 C |
| Modulus of Elasticity in Tension | 18000 ksi | 124100 Mpa |
| Modulus of Rigidity | 6000 ksi | 12410 Mpa |
Technical Specifications:
| Hollow Rods | Min Bore Size 20 mm and Max OD 100 mm |
| Round Rods | 8mm To 100 mm |
| Hex | 10mm To 60mm |
| Square | 10mm To 60mm |
| Flat | 10mm Min Thickness and max Width 120mm |
| Billets | Up to 200 mm |
| Ingots | As per Specification |